ET5401 Toughened High-Temperature Resistant Two-Part Epoxy, Amber, 400ml Cartridge

Permabond® ET5401 is a two-part, 2:1 mixable, semi-flexible toughened no-slump epoxy adhesive with good adhesion to a variety of substrates such as wood, metal, ceramics, and some plastics and composites. Permabond ET5401 forms tough bonds providing high peel resistance and high shear strength coupled with excellent resistance to high temperatures. ET5401 performance is enhanced by curing at high temperatures or being exposed to high temperatures (such as during paint-stoving).

Adhesion to a wide variety of substrates
Full cure at room temperature
Easy to apply
High shear and peel strength
Good impact strength
High-temperature resistance
Non-drip rheology

$110.67

Buy 2 for $107.35
Buy 6 for $104.03

Skip to the beginning of the images gallery

Technical Documents

Product Info & TDS Sheets

Permabond ET5401 Technical Data Sheet

Details

Physical Properties of Uncured Adhesive

	ET5401A	ET5401B
Chemical composition	Epoxy Resin	Polyamine Hardener
Appearance	White	Black
Viscosity @ 25°C	20rpm: 60,000-120,000 mPa.s (cP) 2.5rpm: 250,000-450,000 mPa.s (cP)	20rpm: 50,000-100,000 mPa.s (cP) 2.5rpm: 150,000-250,000 mPa.s (cP)
Specific gravity	1.2	1.4

Typical Curing Properties

Mix ratio by volume: 2:1
Maximum gap fill: 5mm 0.2 in
Usable / pot life @23°C: 10-12 mins
Handling time @23°C (to 1 N/mm²): 60-90 mins
Working strength @23°C: 24-48 hours
Full cure @23°C: 4-7 days

Typical Performance of Cured Adhesive

Shear strength (grit blasted mild steel)* ISO 4587 Cured 25°C for 7 days: 10-15 N/mm² (1450-2200 psi)
Shear strength ISO 4587 Cured 80°C for 1 hour:
- Mild steel 20-30 N/mm² (2900-4400 psi)
- Aluminium 20-25 N/mm² (2900-3600 psi)
- FRP Glass Polyester: 6-8 N/mm² (900-1200 psi)
- FRP Glass Epoxy: 19-23 N/mm² (2800-3300 psi)
- Carbon Fibre: 22-24 N/mm² (3200-3500 psi)
Peel Strength (aluminium)* Cured 80°C for 1 hour: 140-160 N/25mm (31-35 PIW)
Peel Strength (aluminium)* Cured 200°C for 15 mins: 250-300 N/25mm (55-66 PIW)
Hardness (ISO868):
- 65-75 Shore D (cured at 25°C)
- 75-85 Shore D (cured for 1hr at 80°C)
Elongation at break (ISO37): 4-8%
Glass transition temperature Tg:
- Heat cured: 110°C (230°F)
- Room temp. cure: 50°C (122°F)
Dielectric strength: 15-25 kV/mm