801 High-Temperature Wicking Grade Cyanoacrylate Adhesive, Clear, 1 oz. Bottle

Permabond® 801 is a low-viscosity modified ethyl cyanoacrylate suitable for applications where high-temperature resistance is required. This material is fast-setting and has good adhesion to rubber, metal, and plastics. Cyanoacrylate adhesives are single-component adhesives that polymerize rapidly when pressed into a thin film between parts. The moisture adsorbed on the surface initiates the curing of the adhesive. Strong bonds are developed extremely fast and on a great variety of materials. These properties make Permabond® cyanoacrylates the ideal adhesives for high-speed production lines.

High-temperature resistance
Rapid curing
Ease of use - no mixing or heat cure
100% reactive, no solvents

$34.80

Buy 2 for $33.76
Buy 6 for $32.71

Skip to the beginning of the images gallery

Technical Documents

Product Info & TDS Sheets

Permabond 801 Technical Data Sheet

Details

Physical Properties of Uncured Adhesive

Chemical composition: Ethyl cyanoacrylate
Appearance: Colourless
Viscosity @ 25°C: 10-15 mPa.s (cP)
Specific gravity: 1.1

Typical Curing Properties

Maximum gap fill: 0.05mm (0.002")
Fixture/handling time* (0.3 N/mm² shear strength is achieved):
- 10-15 seconds (Steel)
- 10-15 seconds (Buna N Rubber)
- 10-15 seconds (Phenolic)
Full strength: 24 hours

*Handling times can be affected by temperature, humidity, and specific surfaces being bonded. Larger gaps or acidic surfaces will also reduce cure speed but this can be overcome by the use of Permabond C Surface Activator (CSA) or Permabond QFS 16.

Typical Performance of Cured Adhesive

Shear strength** (ISO4587)
- Steel 19-23 N/mm² (2800-3300 psi)
- ABS >6 N/mm² (>870 psi)*
- PVC >10 N/mm² (>1450 psi)*
- Polycarbonate 6 N/mm² (870 psi)
Coefficient of thermal expansion: 90 x 10^-6mm/mm/°C
Coefficient of thermal conductivity: 0.1 W/(m.K)
Hardness (ISO868): 85 Shore D
Dielectric Strength: 25kV/mm